The term “killed” indicates that the steel has been sufficiently deoxidized to quiet the molten metal when poured into the ingot mold. The general practice is to use aluminum ferrosilicon or manganese as deoxidizing agents. A properly killed steel is more uniform as to analysis and is comparatively free from aging. However, for the same carbon and manganese content Killed Steel is harder than Rimmed Steel. In general all steels above 0.25% carbon are killed, also all forging grades, structural steels from 0.15% to 0.25% carbon and some special steels in the low carbon range. Most steels below 0.15% carbon are rimmed steel.